- The composite hardness was increased comparing to copper due to the reinforcement effect of nanosized al2o3 . and the density was related with the parameters of hot - press sintering processing . the dry sliding wear of the composites was investigated in a pin - on - disk wear test rig
在自制的销?盘式低载荷摩擦磨损试验机上对复合材料进行摩擦磨损实验，通过对实验数据和sem形貌的分析，表明纳米al _ 2o _ 3陶瓷颗粒增强铜基复合材料有较好的抗磨损性能。 - The results show that the composites were more wear resistant than the matrix , contributing to the " volume effect " and " size effect " , the wear resistance increases with the particle content and size . the composite shows better wear resistance than high chromium cast iron material especially in low load and fine abrasive test condition . the results also indicate that the composite strengthened by ageing treatment was more wear resistant than as - cast composite
磨损试验结果表明，铸造碳化钨颗粒增强cu - ni - mn合金基复合材料具有比较高的抗磨料磨损能力，而且其耐磨性随着铸造碳化钨颗粒体积分数及尺寸的增大而提高，表现出了强烈的“体积效应”及“尺寸效应” ，尤其是在低载荷、细磨料磨损条件下，复合材料表现出更好的而寸磨性，即使与高铬铸铁( cr28 )相比也有很大程度的提高。 - Under special conditions such as low partial load / deep vacuum , unexpected high air leakage resulting in a major temperature difference ( above 10 c ) between the steam exhaust turbine temperature and all air - take off temperature measurement , the suction capacity can be improved by using 2 main ejector simultaneously
在特殊条件如局部低载荷/极端真空，不正常的热交换，意想不到的高空气泄漏导致的在蒸汽排气温度和抽空温度测量上产生的严重温差（ 10 c以上） ，用两台主抽汽器同时工作可以提高抽气量。