喷射高度的英文
jetting height
例句与用法
- The two constituents project to different heights .
这两种组元的喷射高度不同。 - The conclusions are drawn as following : 1 . regularity of fabrication in aluminum matrix composite ring - shaped performs with large dimensions and effects of parameters were investigated , based on the novel crucible movable spray deposition technology and equipment . the optimal parameters are that the diameter of the delivery tube is 3 . 8mm , spray gas pressure is 0 . 8mpa , spray height is 200mm , and transferring pressure of sic is 0 . 5mpa
通过系统的实验研究得到如下结论: 1 .基于新型的移动坩埚自动化控制喷射沉积环坯制备技术及装置,研究了大尺寸铝基复合材料环坯的制备规律,讨论了喷射沉积工艺参数对沉积坯形成过程的影响,得到了最佳工艺参数:导流管直径d = 3 . 8mm ,雾化气体压力p = 0 . 8mpa ,喷射高度h = 200mm , sic颗粒输送压力p送= 0 . 5mpa 。 - The optimal parameters of making high silicon content aluminum alloys is : spray height is 220 - 230mm , spray angle is 30 ? the scanning velocity of atomizer is 30mm / s , the original offset of the substrate is 30mm , rotation velocity of the substrate is 120rpm , spray gas pressure is l . ompa , the diameter of the delivery tube is 3 . 6mm , the drawing velocity of the substrate will be adjusted on - line with a plc on the basis of the spray
通过对多层喷射沉积原理及工艺参数的研究，得出制备al - 22si - 3cu - 1mg合金的最佳工艺参数为：喷射高度为220mm - 230mm ，基底转速为120rpm ，雾化器扫描速度为30mm / s ，基底下降转速依据喷射情况由智能控制器进行实时调整，喷射角度为30 ，初始偏心距为30mm ，导流管直径为3 . 6mm ，雾化气压为1 . 0mpa 。