复数磁导率的英文

complex magnetic permeability

• 复数:    plural complex num ...
• 磁导率:    magnetoconductivit ...
• 初磁导率 起始磁导率:    initialpermeabilit ...

例句与用法

1. 2 . sr will substitute for ba the quantity increase , the material resonance frequency increases , the will change slightly ; when few zn substitutes for co , with the zn increase , resonance frequency will cut down , the increases , the q value will drop
   2sr取代ba的量增加,材料的截止频率将增大,复数磁导率将变小;当少量zn取代co时,随着zn取代量的增加,截止频率向低频移动,磁导率增加, q值总体下降。
2. From the experimental results , we studied the relationship between the diameter of fiber , the composition of s s and the impacts upon the electromagnetic parameter of fibers . get following conclusions : both the complex permeability and the complex permittivity of ss fibers decreased with the increase of diameter in some region , the complex permittivity of 304 ss fibers , 2 m in diameter , could be up to 2 . 5 at the 2 ghz , the 302 ss fibers had better frequency dispersion properties than others , agreed with the requirements of the wide - band radar absorbing material in the range of 2ghz ~ 12ghz
   西安建筑科技大学硕士学位论文讨论了影响不银矜冈纤维电磁参数的几个因素，实验结果出发研究了纤维直径、成分对纤维电磁参数的影响，得到以下结论:不钾练冈纤维的微波磁导率随纤维直径的减小而增大; 2微米的304不锈钢纤维的复数磁导率p ’ ‘在zgi ]吃处达到2 . 5 ; 302不韧矜冈纤维电磁胜能明显优于其它两种，且频谱特性在2 ~ 1zghz范围内符合对吸收剂频谱特性的要求。