1. By experiments the conclusions were got that the actived carbon electrode could provide better capacitive character in 7mol / l potassium hydroxide solution after activation in ammonia
   通过大量的实验发现氨水活化处理后的活性炭在浓度为7mol l的氢氧化钾溶液中具有良好的电容性能。
2. Finally the conclusion was that the best material was nanophase manganese oxide synthesized with solid - phase reaction . the best electrolyte was potassium hydroxide with the concentration of 1mol / l
   最终发现固相合成法制备的二氧化锰是其中最优的准电容材料，在1mol l的氢氧化钾溶液中性能最优。
3. 3 . the various organic surfactants were adsorbed on the surface of the current collector . the dynamic hydrogen evolution experiment proved that the evolution hydrogen amount of current collector adsorbing organic surfactants was less than without them in 7 . 0m koh solution with zinc power
   在碱性锌锰电池负极集电体上分别吸附不同的有机表面活性物质，用动态析氢实验表征，发现集电体表面吸附有机活性物质在含锌膏的7 . 0m的氢氧化钾溶液中的析氢量变小。
4. Experiment of hydrogen evolution showed that the evolution hydrogen amount of current collector coated by mono - layer plating or double - layer plating was less than without them in 7 . 0m koh solution with zinc power , and that of the double - layer plating of zn - in , sn - in was the least . cyclic voltammetry - indicated that there is an obvious reduction peak of hydrogen at the potential of about - 0 . 8v vs
   用动态析氢实验表征，发现沉积单、双层金属的集电体在含锌粉的7 . 0m的氢氧化钾溶液体系中的析氢量比无沉积层的铜集电体析氢量要小，其中，沉积锌铟、锡铟双层的析氢量最小。