氧腐蚀的英文

oxygen corrosion

oxygen-type corrosion

• 氧:    oxygen
• 腐蚀:    corrode; corrosion ...
• 耗氧腐蚀:    oxygen-consumption ...

例句与用法

1. The oxygen corrosion behavior of s 135 drill pipe steel in drill fluid
   135钻杆钢在钻井液中的氧腐蚀行为
2. The major reasons for impeller failure were interactive action of coarse microstructure and oxygen corrosion as well as erosion - corrosion
   结果表明，叶轮失效的主要原因是材料组织粗大以及氧腐蚀和冲蚀磨损交互作用的结果。
3. Internal corrosions of the oil storage tanks are caused by oxygen - absorbed , salt and deposits , the last kind of corrosion is most serious
   原油储罐的内壁腐蚀原因为吸氧腐蚀、盐类腐蚀和原油沉积造成的垢下腐蚀，而且原油沉积造成的垢下腐蚀最严重。
4. In this article , the cause of oxygen corrosion occurred at the water inlet in the waste heat boiler without the mea - sure of removing oxygen and the problem of water shock were dis - cussed
   本文对没有除氧措施的余热锅炉气包进水管发生的氧腐蚀及由此产生的气包水冲击问题进行了探讨。
5. In the article , it states another model of oxygen corrosion - corrosion caused by dissolving oxygen , it causes damage on the metal wall surface by oxygenation when the oxygen content in the water is much higer and it is affected by some extra factors ( such as temperature , degree of the acid and the basicity , the content of solid , the water power of scouring and so on )
   本文讲述的是另一种形式的氧腐蚀溶解氧的腐蚀，即由于水中氧含量较高在一定外加条件作用下（如温度、酸碱度、固含量、水力冲刷等）而引起金属壁面的氧化破坏。