包埋料的英文

发音:

"包埋料"怎么读用"包埋料"造句

英文翻译手机版

investment

"包"英文翻译 wrap
"料×"英文翻译 7 chi
"包埋剂,包埋料" 英文翻译 : embedding material
"包埋料液" 英文翻译 : liquid investment
"包埋料用液" 英文翻译 : liquid for investment
"高温包埋料" 英文翻译 : high temperature investment
"硅基包埋料" 英文翻译 : silica-bonded investment
"嵌体包埋料" 英文翻译 : inlay investment
"铸造包埋料" 英文翻译 : casting investment
"磷酸盐包埋料" 英文翻译 : phosphate investment
"石膏基包埋料" 英文翻译 : gypsum-bonded investment
"铸造用包埋料" 英文翻译 : casting investment material
"方石英嵌体包埋料" 英文翻译 : cristobalite inlay investment
"高熔铸金包埋料" 英文翻译 : high melting casting metal investment
"石膏型铸造包埋料" 英文翻译 : gypsum-bonded casting investment
"中溶铸金包埋料" 英文翻译 : mild fusing metal casting investment
"高热包埋料, 高热围模料" 英文翻译 : high temperature investment
"磷酸盐型铸造包埋料" 英文翻译 : phosphate-bonded casting investment
"氧化硅型铸造包埋料" 英文翻译 : silica-bonded casting investment
"包埋" 英文翻译 : embedding; embedment; imbedding; imbedment; inclusion; investing; investment
"包埋埋置" 英文翻译 : imbed
"包埋, 围模" 英文翻译 : investing
"包埋，埋植" 英文翻译 : embedding
"包埋，埋置" 英文翻译 : embedding
"包埋，植入" 英文翻译 : embed

例句与用法

Dental ethyl silicate bonded casting investments
牙科硅酸乙脂粘接注塑包埋料
Dental brazing investments iso 11244 : 1998 ; german version en iso 11244 : 1999
牙科用钎焊包埋料
The composition and properties of three types of titanium investment materials are examined by x - diffraction apparatus , hydraulic pressure tester and thermal expansion coefficient apparatus , respectively
摘要应用x射线衍射仪、液压试验机和热膨胀仪检测国外三种体系铸钛专用包埋料的组成和性能。
The results show that : the fillers of sio2 based investment consist of sio2 , al2o3 and mgo , and the binder is nh4h2po4 for sio2 based investment , the bulk density and the compression strength decrease , the apparent porosity and the thermal expansion increase , when the specimens are heated to 900 ; the fillers of al2o3 based investment consist of al2o3 and mgo , and the binder is nh4h2po4 ; for al2o3 based investment , the bulk density decreases and the apparent porosity increases when the specimens are heated to 900 ; the fillers of mgo based investment consist of mgo and al2o3 , and the binder is ca cement ; for mgo based investment , the compression strength decreases and the thermal expansion increases greatly when the specimens are heated to 900
结果表明：氧化硅系包埋料的骨料是氧化硅、氧化铝、氧化镁，结合剂为磷酸二氢铵，其900锻烧后显气孔率增加，体积密度下降，耐压强度降低，热膨胀增大；氧化铝系包埋料的骨料是氧化铝和氧化镁，结合剂为磷酸二氢铵，其900烧后显气孔率增加，体积密度下降，热膨胀变化不大；氧化镁系包埋料的骨料是氧化镁和氧化铝，结合剂是铝酸钙水泥，其900烧后耐压强度明显降低，热膨胀明显增大。